NCM622 Aluminum Foil Double Side Coated by LiNiCoMnO2

Size: 241mm L x 200mm W x 0.1mm T

Package: 5 sheets/bag

This electrode sheet is based on Aluminum foil coated by Lithium Nickel Manganese Cobalt Oxide (NCM622) on double sides and can be used as the cathode of Li-Ion battery

Specifications

Material: LiNiCoMnO2 6:2:2)
Current collector (substrate): Aluminum foil (16 microns, area desnityof 4.22mg/cm2)
Coated Area: 241mm L x 175mm W. The edge width of blank area is 12.5 mm for each side.
Double sides area density: 22 ± 0.4 mg/cm2
Compaction density: 3.3 ± 0.1 g/cm3
Coating Thickness: ~67 um
Total Thickness: ~83 um
Active Material Weight: 9.05 g
Active Material Proportion in Powder: 97.5% (PVDF and Super P is and 1% and 1.5% , respectively)
Specific Capacity: 170 mAh/g [0.1C, 3.0-4.3 V vs Li/Li+, Half Cell] [Electrolyte:1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC]

Note: The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.