Aluminum Foil Double Side Coated by LiNiCoMnO2
  • Li-Ion Battery Cathode - Aluminum Foil Double Side Coated by LiNiCoMnO2 (Ni:Co:Mn=8:1:1, NCM811)

Size: 241mm L x 200mm W x 0.1mm T

Package: 5 sheets/bag

This electrode sheet is based on Aluminum foil coated by Lithium Nickel Manganese Cobalt Oxide (NCM811) on double sides and can be used as the cathode of Li-Ion battery

Specifications

  • Material: LiNiCoMnO2 8:1:1)
  • Current collector (substrate): Aluminum foil (16 microns, area desnityof 4.22mg/cm2)
  • Coated Area: 241mm L x 175mm W. The edge width of blank area is 12.5 mm for each side.  
  • Double sides area density: 21 ± 0.4 mg/cm2
  • Compaction density: 3.3 ± 0.1 g/cm3
  • Coating Thickness: ~64 um
  • Total Thickness: ~80 um
  • Active Material Weight: 8.41 g
  • Active Material Proportion in Powder: 95% (PVDF and Super P is 2% and 3%, respectively) 
  • Specific Capacity: 190 mAh/g [0.1C, 3.0-4.3 V vs Li/Li+, Half Cell] [Electrolyte:1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC]

Note: The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.