* Material:  LiNiCoMnO2  (Ni:Co:Mn = 5:2:3)

* Current collector (substrate): Aluminum foil ( 15 microns)

* Cathode material: Lithium Nickel Manganese Cobalt Oxide

* Coated Area: 241mm L x 200mm W. The edge width of blank area is 12.5 mm for each side.  

* Double sides material density: 23.0 mg/cm2

* Compaction density: 3.0 g/cm3

* Active Material Weight: 10.9878g

* Active Material Proportion in Powder: 95.5% (PVDF and Super P is 2% and 2.5%, respectively) 

* Specific Capacity: 155 mAh/g (0.2C, 4.2-2.7 V vs Li/Li+, Half Cell)

Average Cycle Life: 500 Cycles @ 0.2C Charging/Discharging Rate [Electrolyte:1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC]

Length: 241mm

Width: 200mm

Thickness: 103um +/- 5um
Foil Thickness: 15um +/- 5um
Coating Thickness: 88um +/- 10um (double side coated)

Net Weight: 27.5g

Double side coated

Qty: 5 sheets/bag

Note: The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation